Flying Whale H54-52 Phenolic Epoxy Electrostatic Lead Paint
Product overview
A two-component coating made of epoxy resin, anti-rust pigment, electrostatic conductive material, filler, curing agent and various additives, solvents, etc. The paint film has excellent electrostatic conductivity, excellent salt spray resistance, water vapor resistance, oil resistance and other corrosion resistance.
Recommended use
Applicable to the use of electrostatic conductive coating on the inner wall of finished oil tank
Product Information
|
Color
|
Light gray and other light colors |
|
Gloss
|
No light |
| Component B (curing agent) | H54-52 phenolic epoxy static paint curing agent |
| Volumetric solids | 74±3% |
| Recommended dry film thickness | 100 microns/approx. 135 microns wet film thickness |
| Theoretical coating rate | 5.03 m2/kg (100 micron dry film meter) |
| Volatile Organic Compounds (VOC) | 242g/L |
|
DensityNote
|
Approximately 1.47kg/l |
Dry data
| Substock temperature | 5 ℃ | 10 ℃ | 23℃ | 35℃ |
|
Paint film surface dry Solid paint film Mixed life |
4 hours 36 hours 6 hours |
3 hours 24 hours 4 hours |
2 hours 16 hours 3 hours |
1 hour 8 hours 2 hours |
Overcoating data
| Substock temperature | 5 ℃ | 10 ℃ | 23℃ | 35℃ |
|
Minimum coating interval Maximum coating interval |
36 hours 7 days |
24 hours 7 days |
16 hours 7 days |
8 hours 5 days |
Note: 1. The above data are for reference only. The actual drying time and the length of the re-coating interval depend on the film thickness, ventilation, humidity, lower paint and mechanical strength, etc.
2. The surface of the paint film before recoating must be clean and dry, free of pulverization and other pollutants. If necessary, the surface before recoating should be fully napped.
Construction parameters
| Mixing | Use a power mixer to stir component A evenly, and then add component B while stirring until fully mixed. |
| ripening | At the temperature below 10 ℃, aging for 15 minutes |
| mixing ratio | Component A: Component B = 20:4.4 (weight ratio) |
| Thinner/cleaning agent | Flying Whale X-103 Thinner |
| airless spraying |
Nozzle diameter: 0.53~0.64mm Nozzle pressure: 10 ~ 25MPa Dilution ratio: 0 ~ 5% (by weight) |
| Gas spraying | The use of suitable special equipment, spraying when the need for dilution |
| Brush/Roller | Applicable, recommended for pre-coating and small-scale coating |
CONSTRUCTION CONDITIONS
The substrate temperature shall be at least 3 ℃ higher than the air dew point, and the relative humidity shall be lower than 85%. The measurement of temperature and humidity should be carried out at the substrate near the operation point. When the construction is not in an open space, good ventilation must be provided to ensure the normal drying of the paint film.
Surface treatment
Remove oil, soluble salt, floating ash, water and other dirt on the surface to be coated;
Steel with oxide scale: sandblasting to Sa2.5;
Steel without oxide scale: sand blasting to Sa2.5 or grinding wheel to St3;
Typical supporting
| H54-52 phenolic epoxy electrostatic conductive paint | 3 x 100 microns (dry film thickness) |
For more scope of use, please consult Flying Whale New Material Company.
Safety and Health
Before using this product, please pay attention to the safety label on the packaging container, refer to and follow the information and precautions related to health and safety in the product safety technical manual of flying whale new material company. During the construction and drying of the product, appropriate ventilation and preventive measures must be adopted to control the solvent concentration within the safety limit to prevent poisoning or hypoxia. Take measures to avoid skin and eye contact with the product. If contact occurs, wash it immediately with suitable detergent, soap and water. If splashed into eyes, rinse with water and seek medical treatment immediately.
Packing specification
| Packing barrel specification | Packing weight | |
| Group A | 20 Litres | 20kg |
| Component B | 5 Litres | 4.4kg |
Storage period
Store in a cool, dry, ventilated and dedicated warehouse away from heat sources. Under normal temperature conditions, the storage period is 12 months, and then it needs to be used after passing the inspection.
Precautions
Corporate Statement
The above information and data of this product are accumulated according to our test and actual use experience, which can be used as a construction guide. For the construction carried out without our knowledge, we only guarantee the quality of the paint itself and are not responsible for any product performance problems arising from other aspects. We have the right to modify this manual according to the continuous improvement of the product.
Supplementary Notes
Key words:
The bottom of the ship and the waterline parts with anti-fouling requirements.
Waterline and freeboard
Deck part
Superstructure
Ballast tank
Living Cabin
Battery compartment
Drinking water tank
Pretreatment of steel plate
Oil tank
More products
Leave us a message
Zone B, Zhanmao Industrial Zone, Putuo District, Zhoushan City, Zhejiang Province
T: 86-0580-3080992,86-0580-6629666
F: 86-0580-3095713
E: zjfj1985@126.com
©2023 Zhejiang Feijing New Material Science & Technology Co.,Ltd.